| CJ-36 IGV |
| |
| Asbestos Gasket Jointing Sheet With Wire |
|
 |
| Material Composition: |
| Made from Chrysotite Asbestos
Fiber with Synthetic Oil & Solvent resistant
elastomers with MS Wire Reinforced |
| |
| Applications: |
| To seal off alcohols, water, air,
steam, oils, fuels, etc. This grade is specially
suitable for internal combustion engines, compressors,
pipe - lines and several other industrial applications
under high stress conditions |
| |
|
 |
|
| |
| THICKNESS
|
: |
0.60 mm to 6.00 mm. |
| SURFACE FINISH |
: |
Grey, Graphited |
| DIMESNSION OF SHEETS |
: |
1500MM X3100MM, 1500MM X1500MM, 1500MM X
1000MM, 1500MM X 2000MM, 1270MM X1270MM, 1270MM X 3810MM
|
| OPERATING CONDITION |
: |
Maximum pressure : 200 Kg/cm2
Maximum Temperature : 600°C |
|
| |
| The following Information Applies to
material Thickness 1.5mm. |
| |
| S.NO. |
Typical Properties |
Test Method |
Unit |
Specified Value |
|
1 |
Density |
IS:2712/1998 |
g /cm3 |
1.70 - 2.20 |
|
2 |
Tensile Strength |
IS:2712/1998 |
Mpa |
>26.0 |
|
3 |
Compressibility |
IS:2712/1998 |
% |
6 – 14 |
|
4 |
Recovery |
IS:2712/1998 |
% |
>40 |
|
5 |
Ignition Loss |
IS:2712/1998 |
% |
<26 |
|
6 |
Stress Resistance |
IS:6210/1979 |
Mpa |
>23 |
|
7 |
FLUID ABSORPTION |
|
|
|
|
|
IN ASTM OIL NO.3 |
|
|
|
| |
(a)
Thickness Increase |
IS:2712/1998 |
% |
< 25 |
| |
(b) Mass
Increase |
IS:2712/1998 |
% |
< 20 |
| |
IN
FUEL B |
|
|
|
| |
(a)
Thickness Increase |
IS:2712/1998 |
% |
< 20 |
| |
(b) Mass
Increase |
IS:2712/1998 |
% |
< 20 |
| |
IN
WATER |
|
|
|
| |
(a) Mass - Increase |
IS:2712/1998 |
% |
< 10
|
|
|
| NOTE |
| All information and recommendations given
in this brochure are correct to the best of our knowledge.
However, in view of the wide varsity of possible installation
and operating conditions one cannot draw the final conclusion in
all application cases regarding the behaviour in a gasket joint.
Therefore, information can only serve as a guideline. |
| |
|
|
|
|